Professional Design Constantan Manufacturers China - Nickel 201 – Phoenix Alloy
Professional Design Constantan Manufacturers China - Nickel 201 – Phoenix Alloy Detail:
Nickel 201 has lower concentration of carbon that avoids embrittlement due to intergranular corrosion at temperatures up to 600oF. It offers similar corrosion resistance properties as of Nickel 200 alloy however it provides better performance in the elevated temperature applications. The alloy 201 provides excellent resistance to oxidizing and reducing conditions, acids, alkalines, salts, fluorine and chlorine solutions. Nickel 201 alloy is utilized in the applications at temperatures above 600oF.
Mechanical Property Requirements
|Ultimate Tensile||Yield Strength (0.2% OS)||Elongation.|
|Min||50 KSi||10 KSi||40|
|Min||345 MPa||70 MPa|
Product detail pictures:
Related Product Guide:
Forging For Nickel Alloys
3 Ways to Nickel Plate
We insist on offering good quality generation with very good business enterprise concept, honest income as well as best and fast assistance. it will bring you not only the premium quality product or service and huge profit, but probably the most significant is usually to occupy the endless market for Professional Design Constantan Manufacturers China - Nickel 201 – Phoenix Alloy, The product will supply to all over the world, such as: Venezuela, Haiti, Munich, By integrating manufacturing with foreign trade sectors, we can provide total customer solutions by guaranteeing the delivery of right products to the right place at the right time, which is supported by our abundant experiences, powerful production capability, consistent quality, diversified product portfolios and the control of the industry trend as well as our mature before and after sales services. We'd like to share our ideas with you and welcome your comments and questions.
By Monica from Morocco - 2015.06.28 19:27
The goods we received and the sample sales staff display to us have the same quality, it is really a creditable manufacturer.
By Nydia from Turin - 2015.10.09 19:07